| Degree of acetalization: | medium |
| Solution viscosity: | very low |
| Residual PVA content: | medium |
| Specification viscosity (10% ethanol) Hoeppler method (20°C): | 9,0 - 13,0 mPa*s |
| Corresponding viscosity range2 (10 % ethanol/ toluene 1:1) Brookfield method (20°C/30 rpm): | 6,5 - 8,5 mPa*s |
| PVOH content (Hydroxyl): | 14,0 - 18,0 wt % |
| PVOH content (Hydroxyl): | 21,0 - 26,5 mol % |
| PVOAc content (Acetate): | 5,0 - 8,0 wt % |
| PVOAc content (Acetate): | 3,8 - 6,0 mol % |
| Glass transition temperature = Tg: | 60 °C |
| Solid: | >= 97,5 wt % |
1) 5 % Viscosity
2) Calculated
Call For Experience
Gurshranjit Singh
Technology Scouting
Phone: +49 69 305 85729
E-Mail: gurshranjit.singh@kuraray.com
Main application Area
- Strippable packaging coatings
- Corrosion protection/shop primers/wash primers
- Heat-sealable lacquers
- Radiator primers/topcoats
- Wood sealing varnishes
- Plastic surface finishes/nitrocellulose lacquers
- Gear paints/paper varnishes
- Adhesives/oil-resistant lacquers
- Road marking paints
- Additive for powder coatings
- Coil coatings
- Inkjet printing inks
- Flexographic/special gravure inks
- Pigment preparations
- Hotmelts
- Cardboard packaging impregnations
- Thermoplastic processing
Possible application Area
- Automotive refinishing coatings
- Can coating/Stoving enamels/Film lacquers
- Zinc-rich primers
- Thermo-transfer inks
- Adhesive additives/rheology modifiers
- Light bulb cement
- Structural adhesives
- Candle coatings