MOWITAL® G 36

CONTACT US NOW

MOWITAL® G = granulated polyvinyl butyral

Non-volatile content (according to DIN 53216): ≥ 99,5 %
Content of polyvinyl alcohol (according to DIN 53240): 18–21 %
Content of polyvinyl acetate (according to DIN EN ISO 3681): 1-4 %
Viscosity in solution (viscosity in 10 % ethanol at 20 °C): 30–280 mPa*s
MFR (2,16 kg/190 °C, according to ISO 1133): 95,1–22 g/10 min
Tg (DSC, according to ISO 11357-1): 70–72 °C
Softening temperature (ring and ball method, DIN EN ISO 4625): 140–210 °C
E-modulus (according to ISO 1269 at 105 °C): 2480–2750 N/mm2
Yield strength (according to ISO 1269 at 105 °C): 55–60 N/mm2
Bulk density (according to ISO 60): 600–750 g/L
Charpy impact (not notched) (according to DIN EN ISO 179): 107–110 KJ/m2
Charpy impact (notched) (according to DIN EN ISO 179): 2-4 KJ/m2
Vicat B 120 (according to DIN EN ISO 306): 55-73 °C
Shore D (according to DIN ISO 868): 79-83 wt %
Contactbox: Gurshranjit Singh | Technology Scouting of the Mowital® Brand

Call For Experience

Gurshranjit Singh

Technology Scouting
Phone: +49 69 305 85729
E-Mail: gurshranjit.singh@kuraray.com

 

 

or use our contact form 

Main application Area

  • appropriate for 3D-printing
  • suitable for thermoplastic processing (injection moulding and extrusion processes)
  • compatible with various plastics, e.g. PMMA, PA, PVC, ABS, TPU, or thermoplastic elastomers
  • use as compatibiliser and dispersing additive for pigments, inorganic fillers, metal particles
  • adhesion promoter (glass, metals, wood, ceramics, etc.)
  • use for formulations with high-colour purity
  • reactivity of free OH-groups (cross-linking, base for chemically modified PVB-binders)
  • compliance with food regulations

 

 